GB15256-2014塑料低溫脆化試驗機檢查電線之塑料外殼以及硫化橡膠在低溫測試時的脆化特性。

The embrittlement of plastic case of the wire and the embrittlement of vulcanized rubber during low temperature test.

用戶可以選擇TS-BC直線性沖擊試驗方法或者TS-BT擺錘型沖擊試驗方法以滿足客戶對設備的不同需求。

The user can choose the TS-BC linear impact test method or TS-BT pendulum type impact test method to meet the customer's different needs of the equipment.

試驗時將試樣固定于夾具上，然后將試樣浸泡坐在低溫介質中5分鐘，用2±0.2m/s的線速度沖擊試樣，zui后檢查試樣在zui低溫度是否出現裂紋、裂縫、小孔、以及是否完分離成碎片。

Test sample is fixed on the fixture, then soaked samples sitting in low temperature medium in 5 minutes, with 2 + 0.2 M / s line speed impact test specimens, the final inspection sample in the lowest temperature whether cracks, cracks, holes, and whether separates into pieces.

GB15256-2014塑料低溫脆化試驗機通過轉換卡盤托架底座可以連續的進行樣品測試，可以節省樣品放回原處時間，滿足很多樣品各自的測試標準。

Through the conversion of the chuck bracket base can be continuous sample test, can save the sample back in place of time, meet a lot of samples of the respective test standard.

塑料低溫脆化試驗機制冷方式 The refrigeration mode of multifunctional plastic cryogenic embrittlement test machine
采用二段式壓縮機快速降溫制冷，zui低溫度可達-76℃(如需低于-76℃，可定制)。

Two stage compressor cooling refrigeration, the lowest temperature of up to -76 (for example, can be customized for less than -76).

溫度可控性高，低溫槽中液體傳熱介質可啟用攪拌馬達，使溫度均勻性更佳。毎次可測試4組試樣， 旋轉定位夾具對每組試樣進行沖擊測試，檢査出現脆性破壞的zui低溫度。

The temperature can be controlled and the heat transfer medium of the liquid in the cryogenic tank can be used for stirring the motor, and the temperature uniformity is better.. Each time 4 groups of samples testing, rotary positioning fixture for each specimen of impact test and laboratory examination appear brittle failure of minimum temperature.

測試標準：

Standard for testing of multi - functional plastic cryogenic Embrittlement Testing Machine:

GB/T5470-2008塑料沖擊法脆化溫度的測定

Determination of embrittlement temperature of plastic impact method

GB/T 12584-2008橡膠或塑料涂覆織物低溫沖擊試驗

Low temperature impact test for rubber or plastic coated fabrics

GB/T15256-1994硫化橡膠低溫脆性的測定（多試樣法）

Determination of low temperature brittleness of vulcanized rubber (Multi - specimen method)4

ISO 812-2011硫化橡膠或熱塑性橡膠--低溫脆性的測定

Vulcanized or thermoplastic - Determination of low temperature brittleness

BS 903 A25:1992 橡膠的物理試驗.第A25部分:低溫脆性測定

Physical tests for rubber - Determination of low temperature brittleness for part A25

ISO 974-2000塑料.沖擊脆化溫度的測定

Plastics. Determination of impact embrittlement temperature

ASTM D2137-2010撓性聚合物及其涂覆織物脆化點測試方法

Test method for brittle point of flexible polymer and its coated fabric

ASTM D746-2013用沖擊法測定塑料及彈性材料脆化溫度的試驗方法

Test method for brittle temperature of plastic and elastomeric materials by impact method

JIS K7216塑料低溫脆化測試方法

Test method for low temperature embrittlement of plastics

JIS K6261-2006硫化或熱塑性橡膠--低溫特性的測定

Vulcanized or thermoplastic - Determination of low temperature properties

JIS C3005-2000橡膠或塑料絕緣電線和電纜的試驗方法

Test method for rubber or plastics insulated wires and cable

JIS K 6723-1995增塑聚氯乙烯化合物 Polyvinyl chloride compound

●主要特點：Main features

卡盤轉換部分 Chuck conversion part
4組卡盤通過旋轉手柄時，轉換卡盤能夠啟動進入打擊測試狀態。

The 4 group of chuck by rotating the handle, the conversion can start to enter the test state against chuck
在規定的速度下，通過交替打擊錘打擊卡盤里樣品夾中的樣品。

in terms of speed, by alternay blow hammer in the sample sample clamp chuck.
試驗槽（低溫槽） Test trough (cryogenic tank)
通過利用復疊制冷系統可以冷卻到-80℃。

The -80 can be cooled by using the cascade refrigeration system
控制部分電子電路，設備依照給定的過程進行程序控制，是機器內部固有的

Control part of the electronic circuit, the equipment according to the given process of the procedure control, is inherent in the machine

●技術參數：Low temperature embrittlement testing machine technical parameters - multi functional plastics